Cost-effective Hearting Resistance Alloy FeCrAl 0Cr25Al5 Wire
Chemical composition:
Alloy Nomenclature Performance | 1Cr13AL4 | 0Cr25Al5 | 0Cr21AL6 | 0Cr23Al5 | 1Cr21Al4 | |
Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 |
Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | |
Re | opportune | opportune | opportune | opportune | opportune | |
Fe | Rest | Rest | Rest | Rest | Rest | |
Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | |
Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | |
Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | |
Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | |
Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | |
Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | |
Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | |
Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | |
Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | |
Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | |
Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
continuous service time(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | |
Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | |
Application:Typical applications for 0Cr25Al5 are used in electric ceramic cooktop,industrial furnace,heaters.
Packaging & Delivery
Packaging Details：Products of coils wire,strip and bar are packed with waterproof paper or weave bag, into pallets or wooden case.Products of spool wire or ribbon are packed with plastic film, standard cardboard boxes,into pallets and wooden case.
Special packaging requirements can also be accommodated.
OEM is also acceptable.
Port：Shanghai,Ningbo,Shenzhen,Qingdao,Lianyungang
Lead Time:
Quantity(kilograms) | 1 - 50 | >50 |
Est. Time(days) | 15 | To be negotiated |